6 1/4″  160 mm
Fine tips with special satin finish on tips and grips

Inox Steel type S

• Martensitic higher carbon steel.
• Magnetizable.
• Contains from 12.5 to 14.5 wt% chromium.
• Can be hardened by heat treatment, forming should be done in the annealed condition.
• Less resistant to corrosion than the Austenitic or Ferritic grades.
• Used where strength and/or hardness are of primary concern and where the environment is relatively mild from a corrosive standpoint.
• Typical applications for the electronic industry, watch-makers, jewelers and laboratory and medical applications in mild aggressive chemical environments.

Titanium type TA

• Titanium Grade 1 (unalloyed titanium)
• Engineering materials with extraordinary combination of properties: relatively low density (4.5 g/cm³), good mechanical properties and a very high melting point that allows the use at high temperatures (1600°F, 870°C).
• Good corrosion resistance at room temperature to air, marine and a variety of industrial environments.
• Good cold formability, high ductility.
• Fully non-magnetic.
• Generally it is used when in addition to the corros ion resistance, high strength-to-weight ratio is required.
• Typical applications include handling of components in cleaning/chemical processes also at high temperature, histology, biology, medicine, surgery.